DIN 1.2367 Hot Worked Mold Steel
1. Injection molding: DIN 1.2367 is often used in the production of injection molds for plastic components due to its high wear resistance and ability to maintain its shape under high temperatures and pressures.
2. Die casting: The high hardness and toughness of DIN 1.2367 make it suitable for use in die casting applications, where it can withstand the high temperatures and pressures involved in the process.
3. Extrusion: DIN 1.2367 is also used in the manufacturing of extrusion dies for shaping materials such as plastics, metals, and ceramics due to its excellent wear resistance and thermal conductivity.
4. Tooling: DIN 1.2367 is commonly used in the production of various types of cutting tools, punches, and dies due to its high hardness, toughness, and resistance to wear and deformation.
- HONGXIN
- DAYE
- 30 DAYS
- 8000T/MONTH
- Information
1:DIN 1.2367 steel introduction
The hot work tool steel EN DIN 1.2367 ESR is a chromium-molybdenum-vanadium alloyed hot work tool steel with high
thermal fatigue resistance. It has been refined via ESR process to ensure highest quality standards in terms of grain
size, segregation, micro-cleanliness, and purity. EN DIN 1.2367 features high isotropy, reason for which transversal
resilience is often three times higher when compared to conventional EN DIN 1.2367. Furthermore, the thermal
fatigue resistance is also often much higher than that of conventional hot work tool steel EN DIN 1.2343, enabling
longer die lifetime.
2:DIN 1.2367 steel chemical composition
| Grade | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| DIN1.2367 | 0.35 | 0.40 | 0.30 | 0.50 | 0.03 | 0.03 | 0.30 | 0.50 | 4.80 | 5.20 | 0.40 | 0.60 | 2.70 | 3.20 |
3: DIN 1.2367 steel mechanical properties
1.2367 Chrome–molybdenum–vanadium steel for hardening in oil and in air with very good hardenability, high firmness during the heat and resistance to the tempering, very good toughness and plastic properties during normal and also higher temperatures. Further the steel has a very good resistance to tearing of thermal fatigue and low sensitivity to quick changes of temperature. This hot work die steel is appropriate for the heat treatment also for firmness over 1800 N/mm2 and for tools cooled by water. It is well-workable during the heat and well-workable in the soft-annealed state. At request it can also be delivered in ESR quality.
4: DIN 1.2367 steel overviews
| Size | Round | Dia 12-500mm | |
| Plate/Flat/Block | Thickness 8mm-300mm | ||
| Width 210mm-710mm | |||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | ||
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | ||
| Delivery condition | Forged; Hot rolled; Cold drawn | ||
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | ||
| Payment terms | T/T;L/C;/Money gram/ Paypal | ||
| Trade terms | FOB; CIF; C&F; etc.. | ||
| Delivery time | 30-45 days | ||
| Packing | Standard Packages, or as Customers Request | ||
5. Heat Treatment
FORGING: Hot forming temperature: 1080-900oC.
SOFT ANNEALING: Heat to 800-840oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 235.
STRESS RELIEVING: Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
HARDENING: Harden from a temperature of 1030-1080oC followed by air, oil or warm bath (500-550oC) quenching. Hardness after quenching is 53-57 HRC.
TEMPERING:
| Tempering Temperature (oC) | Hardness (HRC) | Tensile Stregth (N/mm2) |
|---|---|---|
| 100oC | 57 | 2140 |
| 200oC | 55 | 1980 |
| 300oC | 54 | 1910 |
| 400oC | 53 | 1845 |
| 500oC | 55.5 | 2010 |
| 550oC | 56 | 2050 |
| 600oC | 53 | 1845 |
| 650oC | 43 | 1360 |
| 700oC | 31 | 995 |
6: Delivery condition
For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed, rough turned.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.
Hongxin Mold Tech Co.,Ltd. owns 1 set of Hot Rolling Production Line at size range flats 8-80*210-710mm, rounds 16-50mm Dia.
12 sets of Hydraulic Forging Hammers from Power 560kgs to 6000kgs which could cover flats 40-300*210-710mm.
8 sets of EF+LF+VD
5 sets of ESR
9 sets of Milling Machines
10 sets of Turning Lathes
6 sets of Precision Milling Machines.
CERTIFICATION: GB/T19001-2016/ISO9001:2015
Products' List
Q1:Are you trading company or manufacturer ?
We are the biggest tool steel factory at Daye & Huangshi. We can provide a wide range of steel products.
Q2:What is alloy steel round bar export packing?
Usually bundling for large diameter,small diameter bars in bulk or as customer's demand.
Q3.What is your MOQ?
We accept small order,if it is stock,any quantities can be accepted.
Q4.What is your lead time?
Depends actual order,around 20-35 days,or negotiation.
Q5.Can you supply sample?
Yes,we can.Sample fee according to your size.
Q6:What certificates do you have?
ISO, ABS, BV, CCS, Dnv, Lr, Gl, Mill Certificate
Q7: How can I get your quotation as soon as possible?
The email and fax will be checked within 24 hours,meanwhile,the Skype,Wechat and WhatsApp will be online in 24 hours.Please send us your requirement,we will work out a best price soon.
Any interests in our company and products, please feel free to contact us for quotation. We warmly welcome you to our factory.