DIN 1.3343 High Speed Tool Steel
DIN 1.3343 is molybdenum based high-speed steel in tungsten–molybdenum series. HSS grade steel M2 is a medium alloyed high speed steel which has good machinability. The H-SS M2 chemical composition gives a good combination of well-balanced toughness, wear resistance and red hardness properties. Widely used for cutting tools such as twist drills, taps, milling cutters, saws, knives etc. Also commonly used in cold work punches and dies and cutting applications involving high speed and light cuts.
- HONGXIN
- DAYE
- 30 DAYS
- 8000 TON/MONTH
- Information
DIN 1.3343 High Speed Tool Steel 
1: DIN 1.3343 Steel equivalent
|
| Grade | C | Mn | P | S | Si | Cr | Mo | v | w | |||||||
| M2 regular C | 0.78 | 0.88 | 0.15 | 0.40 | 0.03 | 0.03 | 0.20 | 0.45 | 3.75 | 4.50 | 4.50 | 5.50 | 1.75 | 2.20 | 5.50 | 6.75 |
| 1.3343 | 0.86 | 0.94 | 0.15 | 0.40 | 0.03 | 0.03 | 0.10 | 0.40 | 3.80 | 4.50 | 4.70 | 5.20 | 1.70 | 2.10 | 5.90 | 6.70 |
| SKH51 | 0.80 | 0.88 | 0.15 | 0.40 | 0.03 | 0.03 | 0.10 | 0.45 | 3.80 | 4.50 | 4.70 | 5.20 | 1.70 | 2.10 | 5.90 | 6.70 |
3: DIN 1.3343 steel mechanical properties
4: DIN 1.3343 steel overviews
| Size | Round | Dia 12-500mm | |
| Plate/Flat/Block | Thickness 8mm~300mm | ||
| Width 210mm-710mm | |||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | ||
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | ||
| Delivery condition | Forged; Hot rolled; Cold drawn | ||
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | ||
| Payment terms | T/T;L/C;/Money gram/ Paypal | ||
| Trade terms | FOB; CIF; C&F; etc.. | ||
| Packing | Standard Packages, or as Customers Request | ||
| Delivery time | 30-45 days | ||
5: Heat Treatment
Anneal
Heat to 1600° F, soak thoroughly at heat. Furnace cool 25° F per hour to 900° F, air cool to room temperature. Approximate annealed hardness 241 Maximum Brinell.
Stress Relief of Unhardened Material: Heat slowly to 1200 to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.
Harden
Heat slowly to 1550° F, soak thoroughly, heat to 1850° F, soak thoroughly. Soak time in the furnace varies from a few minutes to 15 minutes, depending tool size, heat capacity of the furnace, and the size of the charge. – Heat to 2150 to 2200° F for max. toughness and minimum distortion. – Heat to 2250 to 2275° F for max. hardness and abrasion resistance.
Quench
For full hardness, oil quench to 150-200° F. Air quench to 150° F. When quenching in hot salt maintain the quench just above the Ms temperature. After equalizing withdraw parts from the hot salt and air cooled to 150° F.
Temper
Double temper is mandatory, three tempers are sometimes preferred. Soak for 2 hours per inch of thickness. Air cool to room temperature between tempers. The best tempering range for hardness, strength and toughness is 1000 to 1050° F.
| Temper° F | Rockwell “C” | Temper° F | Rockwell “C” |
| As-quenched | 64 | 900 | 64 |
| 400 | 63 | 1000 | 65.5 |
| 500 | 62.5 | 1050 | 63.5 |
| 600 | 62.5 | 1100 | 61.5 |
| 700 | 62.5 | 1150 | 60 |
| 800 | 63.5 | 1200 | 53 |
6. Machinability of AISI M2 Tool Steel H-SS
Shaping of HSS M2 tool steels can be carried out using grinding methods. However, they have poor grinding capability and hence they are regarded as “medium” machinability tool steel under annealed conditions. The machinability of these tool steels M2 is only 50% of that of the easily machinable W group or water hardening tool steels.
7: Delivery condition
For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed, rough turned.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.
Hongxin Mold Tech Co.,Ltd. owns 1 set of Hot Rolling Production Line at size range flats 8-80*210-710mm, rounds 16-50mm Dia.
12 sets of Hydraulic Forging Hammers from Power 560kgs to 6000kgs which could cover flats 40-300*210-710mm.
8 sets of EF+LF+VD
5 sets of ESR
9 sets of Milling Machines
10 sets of Turning Lathes
6 sets of Precision Milling Machines.
CERTIFICATION: GB/T19001-2016/ISO9001:2015
Products' List
Q1:Are you trading company or manufacturer ?
We are the biggest tool steel factory at Daye &Huangshi. We can provide a wide range of steel products.
Q2:What is alloy steel round bar export packing?
Usually bundling for large diameter,small diameter bars in bulk or as customer's demand.
Q3.What is your MOQ?
We accept small order,if it is stock,any quantities can be accepted.
Q4.What is your lead time?
Depends actual order,around 20-35 days,or negotiation.
Q5.Can you supply sample?
Yes,we can.Sample fee according to your size.
Q6:What certificates do you have?
ISO, ABS, BV, CCS, Dnv, Lr, Gl, Mill Certificate
Q7: How can I get your quotation as soon as possible?
The email and fax will be checked within 24 hours,meanwhile,the Skype,Wechat and WhatsApp will be online in 24 hours.Please send us your requirement,we will work out a best price soon.